Method for binding antithrombotic or anticlotting substances to a susceptible material involving the use of an aromatic sulfonyl nitrene

ABSTRACT

A method for binding antithrombotic or anticlotting substances to a susceptible material involving the irradiation of a nitrated aromatic sulfonyl azide contacted with the material, followed by conversion of the nitro group to a diazonium salt and thence coupling of the diazonium salt to a compound which inhibits the clotting or thrombogenic activity of the material. The aromatic sulfonyl nitrene antithrombotic or anticlotting substance intermediate; the intermediate composition of the aromatic sulfonyl nitrene and the material; and the composition of the antithrombotic or anticlotting substance, the aromatic sulfonyl nitrene, and the material are also prepared.

United States Patent [191 Lednicer et al.

[ 1 June 10, 1975 METHOD FOR BINDING ANTITHROMBOTIC OR ANTICLOTTING SUBSTANCES TO A SUSCEPTIBLE MATERIAL INVOLVING THE USE OF AN AROMATIC SULFONYL NITRENE [75] Inventors: Daniel Lednicer, Portage; Edward E. Nishizawa, Schoolcraft, both of Mich.

[73] Assignee: The Upjohn Company, Kalamazoo,

Mich.

[22] 7 Filed: May 30, 1972 21 Appl. No.: 258,016

[52] US. Cl 260/79.3 R; 117/93; 204/159.18; 204/l59.l9; 204/1592; 260/93.7; 260/94.9

GD; 260/94.9 GB; 260/141; 260/152;

[51] Int. Cl. C08f 3/92 [58] Field of Search 260/178, 79.3 R, 94.9 GD, 260/94.9 GB, 198, 200, 207, 776;

[56] References Cited UNITED STATES PATENTS 3,284,436 11/1966 Frisch et al. 260/198 3,413,280 11/1968 De Montmollin et a]. 260/198 X 3,600,377 8/1971 Stingl 260/198 X 3,685,952 8/1972 Renfrew 260/207.1 X 3,844,787 l0/l974 Ulrich et al 96/351 OTHER PUBLICATIONS Breslow, Sulfonyl Nitrenes, Nitrenes, Lwowski, Ed.

Interscience Publishers: New York, 1970, pages 281-284, & 298-299.

Smith, The Chemistry of Open-chain Organic Nitrogen Compounds, (Vol. II), W. A. Benjamin, Inc.: New York, 1966, pages 216-217.

Sidgwicks Organic Chemistry of Nitrogen, Clarendon Press: Oxford, 1966, pages 494-496. Wagner & Zook, Synthetic Organic Chemistry,

John Wiley & Sons, Inc.: New York, 1953, pages 654-657, 764-765, 772-773.

Primary Examiner-Ronald W. Griffin Attorney, Agent, or FirmMartin B. Barancik; Roman Saliwanchik [5 7] ABSTRACT 10 Claims, No Drawings 1 METHOD FOR BINDING ANTITHROMBOTIC OR ANTICLOTTING SUBSTANCES TO A SUSCEPTIBLE MATERIAL INVOLVING THE USE OF AN AROMATIC SULFONYL NITRENE BACKGROUND OF THE INVENTION Technological advances in the last few decades have brought the mammalian body in intimate contact with a variety of devices incorporating foreign materials which were not present in the evolution of theirsysterns. Although many of these devices function as designed, a substantial number of them suffer from serious drawbacks. This appears to be particularly true when a device prepared from a foreign material is in contact with the blood of a mammal. All presently available materials which are in contact with the blood for significant periods of time induce deposition of blood cells and fibrin. This problem has hampered the practical development of artificial organs, extracorporeal shunts, renal dialysis systems, catheters, heart-lung machines and the like. Solution of the problem is also important for in vitro systems such as blood collection and storage containers, for example.

Interaction of blood with the surface of a foreign material can result in two related but distinct processes. The first is a formation of a platelet thrombus which may lead to a second process, namely, coagulation, particularly in areas of slow blood flow. However, coagulation can occur in the absence of platelet interaction, particularly in in vitro systems.

The platelet thrombosis process is initiated by the adherence of blood platelets to the foreign surface with subsequent platelet-platelet interaction or aggregation leading to formation of a thrombus composed almost entirely of platelets. In areas of rapid blood flow, such as the cage of an artificial heart valve or in arterial grafts, the primary difficulty is platelet thrombosis and thromboembolism. Aggregated platelets release a factor which may stimulate a second process, blood coagulation, leading to formation of a fibrin blood clot. Clot formation is of major importance in areas of slow blood flow such as around the sewing ring of a valve or in venous circulation. Although platelet thrombi do not always result in clot formation, they can produce deleterious effects themselves. Since there is not a generic description covering both of these processes, a substance which inhibits platelet aggregation will hereinafter be referred to as antithrombotic and a substance which inhibits fibrin clot formation will hereinafter be referred to as anticlotting.

Previously, researchers have attacked the problem of deposition of blood cells and fibrin on the surfaces of materials primarily by attempting to inhibit clot formation. The most common approach has been to coat the surface or impregnate the material with an anticoagulant, primarily heparin. Because there is no known method of directly binding heparin to materials, the heparin is bound to an intermediate chemical which is also bound to the particular material.

The binding of the intermediate to the material was done initially through adsorption. Since this surface gradually wore off the material, an ionic type of intermediate became employed more frequently. The lifetime of this coating was generally longer but it gradually wore off, as well. Recently, the intermediate compound has been covalently bound to the material. However, this covalent bonding is dependent upon a reactive group such as gamma propylamine in or interspersed within the material, or on radiation grafting.

BRIEF SUMMARY OF THE INVENTION We have now found a new means of covalently bonding antithrombotic or anticlotting compounds to a material. This bonding is brought about by the chemical attachment of the antithrombotic or anticlotting substance to an aromatic sulfonyl nitrene which is chemically bonded to the material, apparently through means of a sulfonamide-type bond. Any material which is susceptible to this type of interaction can have its ability to promote platelet aggregation or fibrin clot formation inhibited.

Therefore, it is in accordance with this invention that we have discovered a method for binding antithrombotic or anticlotting substances to a susceptible material involving the use of an aromatic sulfonyl nitrene.

A further aspect of this invention involves the composition of the antithrombotic or anticlotting substance, the aromatic sulfonyl nitrene, and the material;

DETAILED DESCRIPTION OF THE INVENTION The materials to which antithrombotic or anticlotting substances can be indirectly bound are materials which are susceptible to reaction with an aromatic sulfonyl nitrene. Generally these materials are polymers, either synthetic or natural, with a plurality of carbonhydrogen bonds. The preferable materials include polyethylene, polypropylene, natural or synthetic rubbers, a polyester such as Dacron, nylons, polyurethanes, and the like.

The actual compound which is bound to the surface of the material is the aromatic sulfonyl nitrene. The reaction route appears to be the insertion of the nitrene into a carbon and hydrogen bond of the polymer upon irradiation of an azide, thus forming a sulfonamide. This is illustrated below with a para nitrobenzenesulfonamide.

N-H l Figure l The aromatic sulfonyl nitrene which can be bound to the surface of the material is selected from the group of aromatic sulfonyl nitrenes consisting of Figure ll NI wherein R and R, can be the same or different and are selected from the group consisting of hydrogen, halogen, and normal or isomerized alkyl from one to four carbon atoms, inclusive, and

where R and R, are defined as in FIG. II above and R is a substance which inhibits the thrombotic or clotting activity of the material and is that portion of a substituted aromatic which couples with a diazonium salt. Halogen is fluorine, chlorine, bromine, and iodine. Alkyl is methyl, ethyl, propyl, butyl, and isomers thereof.

Aromatic sulfonyl nitrenes of FIG. II are made from sulfonylchlorides by conversion of the sulfonyl chloride to the corresponding sulfonylazide. The azide is converted to the corresponding nitrene by irradiation. Illustrative sulfonylchloride starting materials for the nitrenes of FIG. II are the following compounds:

2-brom0-5-nitrobenzenesulfonylchloride 2-chloro-4-nitrobenzenesulfonylchloride 2-chloro-5-nitrobenzenesulfonylchloride 4-chloro-2-nitrobenzenesulfonylchloride 4-chloro-3-nitrobenzenesulfonylchloride 4-fluoro-3-nitrobenzenesulfonylchloride 4-propyl-2-nitrobenzenesulfonylchloride 4-tertbutyLZ-nitrobenzenesulfonylchloride 4-propyl-2-chloro-5-nitrobenzenesulfonylchloride 4-nitro-o-toluenesulfonylchloride 5-nitro-o-toluenesulfonylchloride 3-nitro-o-toluenesulfonylchloride 5-chloro-3-nitro-o-toluenesulfonylchloride 2,4-dichloro-5-nitrobenzenesulfonylchloride 4-propyl-6-methyl-2-nitrobenzenesulfonylchloride Illustrative compounds of FIG. III are the aromatic sulfonyl nitrenes of FIG. II with the R compound being that portion of the following illustrative substituted aromatics which couple with a diazonium salt:

8-amino-l-naphthol-5,7-disulfonic acid l-amino-2-naphthol-4-sulfonic acid 4,5-dihydroxynaphthalene-2,7-disulfonic acid 2,3-dihydroxynaphthalene-6-sulfonic acid 7-amino-l-naphthol-3,6-disulfonic acid 8-aminol -naphthol-3 ,6-disulfonic acid l-naphthol-3,6-disulfonic acid 2-naphthol-3,6-disulfonic acid l-naphthol-4-sulfonic acid 2-naphthol-7-sulfonic acid a-methyl-Z-fluoro-Z'-hydroxy-4-biphenylacetic acid a-methyl-2-fluoro-4'-hydroxy-4-biphenylacetic acid The preferred substituted aromatic is 8-amino-lnaphthol-5,7-disulfonic acid.

The preferred R and R substituents of FIG. [I and FIG. [[1 compounds include compounds where R is hydrogen, chloride, bromide, and alkyl from one to three carbon atoms, inclusive.

The most preferred are those compounds where R and R are hydrogen and the nitro group is meta or para.

The compounds and compositions of the invention can be prepared by methods known in the art. The synthesis of FIG. II and FIG. III compounds, aromatic sulfonylnitrene-material intermediate compositions and final compositions of the material-aromatic sulfonyl nitrene-antithrombotic or anticlotting substance will be illustrated employing the meta-nitrobenzenesulfonylnitrene compound. It is to be understood that this compound can be substituted with R and R, as defined above.

Nitrobenzene is chlorosulfonated at the meta position when contacted with chlorosulfonic acid to form meta-nitrobenzenechlorosulfonic acid. The chlorosulfonic acid is then converted to the sulfonylazide by reacting with sodium azide in a solution of aqueous methanol. The compounds of FIG. II and the materialnitroaromatic sulfonyl nitrene intermediate compositions are prepared by irradiating the azide when in contact with a material susceptible to attack by a nitrene. If proper adherence between the material and the aromatic sulfonylazide is difficult to maintain prior to and during the course of irradiation, as with polyethylene, for example, an inert carrier such as Fluorolube 5-30, a perfluorinated mineral oil obtained from Hooker Chemical Company, can be employed in order to maintain the appropriate contact.

The types of radiation which can be employed to convert the azide to the nitrene include ultraviolet, ultrasound, and X-ray. Generally, any radiation which promotes removal of free nitrogen from an azide can be employed. The irradiation time should be of sufficient length to promote the removal of nitrogen from the azide but of insufficient length to cause alteration of the materials desirable characteristics. This irradiation time may vary from an hour or more to a mere flash photolysis.

After formation of the aromatic sulfonylnitrene material composition, the nitro grouping on the aromatic nucleus is conveniently reduced to an amino group by a reduction involving metals, for example, stannous chloride in hydrochloric acid. Sodium thiosulfate in so dium hydroxide is effective as well.

The amino grouping is then diazotized. Nitrous acid prepared in situ by the reaction of sodium nitrite and hydrochloric acid is a suitable reagent for the conversion. Once the diazonium salt is formed, it can be coupled with a substance which possesses antithrombotic or anticlotting activity such as aforementioned. Standard diazonium salt coupling reaction conditions can be employed. The thrombogenic or clotting activity of the material is inhibited by the coating affixed to the material by way of the aromatic sulfonyl nitrene molecule.

lf compounds of FIG. III are desired, a nitroaromatic is reduced to an amino by way of the methods previously stated. The amino group is then diazotized with nitrous acid and the resulting diazonium salt coupled with an antithrombotic or anticlotting substance as aforementioned. This product is then reacted in turn with chlorosulfonic acid and sodium azide. This intermediate compound is then contacted with a material which is susceptible to interaction with a sulfonyl nitrene and then irradiated. The thrombogenic or clotting activity of the material is inhibited by the coating affixed to the material by way of the aromatic sulfonylnitrene. 1

The actual bonding of the aromatic sulfonyl nitrene to the material is difficult to identify since conventional means of crystallization and analysis are not applicable to the system of this invention. Because of the wellknown ability of a nitrene to insert into a carbonhydrogen bond, see D. Breslow in Nitrenes, Lwowski, Ed. lnterscience, N.Y., 1970., and the absence of any reactive groups in polymers such as polyethylene and polypropylene, the most reasonable assignment for the reaction product is that of a sulfonamide.

The following examples are not intended to limit but only to illustrate the invention:

EXAMPLE 1 A solution of 0.6 gram each of mand pnitrobenzenesulfonylazide, the combination of isomers selected so as to reduce crystallinity, and 1.2 milliliters of Fluorolube S-30 oil in 12 milliliters of acetone is prepared. A 15 cm sheet of polyethylene, showing no absorption in the ultraviolet down to 230 nm., is sprayed with one-half of this solution. The sheet is covered with a Vycor plate, an ultraviolet transparent quartz glass, and irradiated for one hour under a low pressure mercury lamp. The sheet is then rinsed with acetone, sprayed with the remaining solution and irradiated with the low pressure mercury lamp for another hour.

The sheet is rinsed with acetone and stirred at room temperature with 10.0 gram of stannous chloride in 100 milliliters concentrated HCl for 4 hours. The sheet is then removed, rinsed with water, stirred for 15 minutes with 1N sodium hydroxide and rinsed again with water.

The sheet is then exposed for two minutes to an ice cold solution of nitrous acid prepared from 50 milliliters of 2.5N HCl and 5 grams of sodium nitrite in 20 milliliters of water. Following a brief rinse with ice water, the sheet is immersed for 2 minutes in a aqueous solution of the monopotassium salt of 8-amino-lnaphthol-5,7-disulfonic acid. This couples the dye to a diazonium salt. The sheet is then washed with acetone and dried and subjected to ultraviolet analysis once more. This sample shows an ultraviolet absorption bond at 250 nm which demonstrates the attachment of a chromaphore.

EXAMPLE 2 A suspension of 3.8 grams of m-toluidine in 4 milliliters concentrated HCl and 20 milliliters of water is cooled in an ice-methanol bath. 2.3 grams of sodium nitrite in a minimum amount of water is added. After 5 minutes, this solution is added to 10 grams of 8- amino-l-naphthol-5,7-disulfonic acid in 50 milliliters of water. The fine precipitate is collected on a filter and vacuum dried to give a dark red powder. Infra red and ultraviolet analysis show this powder to be the coupling product.

1.73 grams of the above prepared powder is added to l0 milliliters of chlorosulfonic acid. After 6 hours of vigorous stirring, the mixture is poured into a small amount of'ice water. The precipitated chlorosulfonate, as identified by I.R., is collected on a filter and vacuum dried.

Two grams of sodium azide in 10 milliliters of H 0 is added to a solution of the sulfonyl chloride. Small aliquots are removed and worked up to monitor for appearance of sulfonyl azide. (lR 2250 cm). When the reaction is complete the cosolvent is removed under vacuum and the residue suspended in a small amount of ice water. The residual reddish solid is then collected on a filter.

The powder is coated on the polyethylene and irradiated in the same manner as Example 1, the nitrene being formed and apparently inserting into a carbonhydrogen bond of the material.

EXAMPLE 3 The following procedures for testing the antithrombotic activity of a coated material is employed in later examples.

A Y-tube extracorporeal shunt is placed between the carotid artery and the jugular vein of a rabbit. When a treated polymer, which can be shaped into a thin flexible sheet, is under study, a small piece of the treated polymer is'placed in one arm of the Y-tube. The other arm is similarly lined with a portion of the non-treated polymer for use as a control. When a treated polymer which is relatively inflexible is studied, a straight section of the treated polymer is connected directly into the carotid jugular by-pass. An untreated control section is placed in tandem.

The animal is given u/kg. of heparin and the shunt is allowed to flow for 1 hour. The Y-tube is disconnected, rinsed gently in Tyrodes solution followed by distilled water and ethanol. The materials are then stained with Luxol Blue, a dye, visually observed and photographed. The platelet deposits on the control and treated polymer are then compared.

EXAMPLE 4 The following procedure for testing the anticlotting activity of a coated material is employed.

A polyethylene or polypropylene test tube is coated with the desired anticlotting substance using the methods employed in this disclosure. Whole blood is collected into these tubes and allowed to clot and assayed by the tilting tube method. Platelet involvement in this reaction Can be minimized by adding an inhibitor of platelet aggregation which does not interfere with blood coagulation. A control tube without a coating and a control tube with a coating of the nitro or amino aromatic sulfonyl nitrene are tested at the same time.

Differences in clotting time from the control tube and the treated tube are measured.

EXAMPLE 5 Following the procedure of Example 1, polypropylene tubing was made nonthrombotic with 8-amino-lnaphthol-5,7-disulfonic acid. The treated tube was then tested for nonthrombogenicity in accordance with the method of Example 3. Virtually no deposit of platelets was observed on the treated polypropylene but substantial deposits were on the control.

EXAMPLE 6 Following the procedure of Example I, polyethylene, Dacron, and latex were made nonthrombogenic with 8-amino-l-naphthol 5,7-disulfonic acid. The treated polyethylene surface was almost devoid of platelets. The treated latex showed substantially less deposit than the untreated control. Since the deposits on the treated tubing were primarily across the lateral portion of the tubing, the deposits may be due to cracks produced by the inversion of the tubing for treatment.

With regard to the Dacron employed, it also appears to have less platelet deposits upon it than upon the control. However, a significant portion of the platelet deposits on the treated Dacron may be due to the Silastic backing on the Dacron, since previous work has shown that the treatment of Silastic with the coating material causes the Silastic to deteriorate, thereby causing greater platelet deposition.

EXAMPLE 7 In accordance with the method of Example 1, a polyethylene sheet is contacted with the m-nitro aromatic sulfonyl azide and irradiated. The resulting treated sheet is tested for nonthrombogenecity in accordance with the method of Example 3. Upon inspection, substantially the same number of platelets are on both the treated and the control sheets. Consequently, a nonthrombogenic effect has not been imparted to the treated polyethylene by the nitro aromatic sulfonyl nitrene.

In like manner, p-amino aromatic sulfonyl azide is contacted with a polyethylene sheet and irradiated. The resulting treated sheet is tested for nonthrombogenecity as in Example 3. A nonthrombogenic effect is not imparted to the treated polyethylene by the amino aromatic sulfonyl nitrene.

These results support the interpretation that it is the antithrombotic substance coupled to the diazonium salt which inhibits the thrombotic effects of the polymeric material.

The small quantity of heparin administered to the subject rabbit does not appear to alter the results of the experiments. Heparin interferes with fibrin formation and does not inhibit the deposition of platelets. Furthermore, since the same animal is used for evaluating both control and treated materials, any effect of heparin appears to be nullified.

We claim:

1. A process for inhibiting the thrombogenic or clotting ability of materials which are susceptible to interaction with an aromatic sulfonyl nitrene which comprises a. contacting the said material with a compound of the generic structure SOzNg wherein R and R are the same or different and are selected from the group consisting of hydrogen, halogen, and alkyl of one to four carbon atoms, inclusive,

b. irradiating the said contacted material and compound of step (a) for a time sufficient to generate a nitrene, V

c. converting the nitro group to a diazonium salt, and

d. coupling the diazonium salt to a compound which inhibits the thrombogenic or clotting activity of the material.

2. A process in accordance with claim 1 wherein the compound to which the diazonium salt is coupled inhibits the thrombogenic activity of the material.

3. A process inaccordance with claim 2 wherein the material is selected from the group consisting of polyethylene, polypropylene, latex rubber and polyethylene terephthalate, R is hydrogen and R is selected from the group consisting of hydrogen, chloride, bromide and alkyl of from one to three carbon atoms, inclusive.

4. A process in accordance with claim 3 wherein the material is selected from the group consisting of polyethylene and polypropylene.

5. A process in accordance with claim 4 wherein R and R are hydrogen.

6. A process in accordance with claim 5 wherein the compound coupled to the diazonium salt is S-amino-lnaphthol-5,7-disulfonic acid.

7. A process for inhibiting the thrombogenic or clotting ability of materials which are susceptible to interaction with an aromatic sulfonyl nitrene which comprises a. contacting the said material with a compound of the generic structure N OaS wherein R and R are the same or different and are selected from the group consisting of hydrogen, halogen, and alkyl of one to four carbon atoms, inelusive, and R is a substance which inhibits the clotting or thrombogenic activity of the said material and is that portion of a substituted aromatic which couples with a diazonium salt, and

b. irradiating the said contacted material and compound of Step (a) for a time sufficient to generate a nitrene.

8. A process in accordance with claim 7 wherein the material is selected from the group consisting of polyethylene, polypropylene, latex, and polyethylene terephthalate, R is hydrogen and R is selected from the group consisting of hydrogen, chloride, bromide and alkyl of from one to three carbon atoms, inclusive, and R is a substance which inhibits thrombogenic activity.

9. A process in accordance with claim 7 wherein the material is selected from the group consisting of polyethylene and. polypropylene, R and R are hydrogen, and R is derived from 8-amino-l-naphthol-5,7- disulfonic acid.

10. A process for inhibiting the thrombogenic or clotting ability of polyethylene which comprises a. contacting polyethylene with a compound of the selected from the group consisting of hydrogen,

genetic structure halogen, and alkyl of one to four carbon atoms, in-

N elusive,

2 b. irradiating the said contacted polyethylene and 5 compound of Step (:1) for a time sufficient to gen- R 1 erate a nitrene,

c. converting the nitro group to a diazonium salt. and d. coupling the diazonium salt to a compound which 5O2N3 inhibits the thrombogenic or clotting activity of the polyethylene. wherein R and R are the same or different and are 

1. A PROCESS FOR INHIBITING THE THROMBOGENIC OR CLOTTING ABILITY OF MATERIALS WHICH ARE SUSCEPTIBLE TO INTERACTION WITH AN AROMATIC SULFONYL NITRENE WHICH COMPRISES A. CONTACTING THE SAIE MATERIAL WITH A COMPOUND OF THE GENERIC STRUCTURE
 2. A process in accordance with claim 1 wherein the compound to which the diazonium salt is coupled inhibits the thrombogenic activity of the material.
 3. A process in accordance with claim 2 wherein the material is selected from the group consisting of polyethylene, polypropylene, latex rubber and polyethylene terephthalate, R is hydrogen and R1 is selected from the group consisting of hydrogen, chloride, bromide and alkyl of from one to three carbon atoms, inclusive.
 4. A process in accordance with claim 3 wherein the material is selected from the group consisting of polyethylene and polypropylene.
 5. A process in accordance with claim 4 wherein R and R1 are hydrogen.
 6. A process in accordance with claim 5 wherein the compound coupled to the diazonium salt is 8-amino-1-naphthol-5,7-disulfonic acid.
 7. A process for inhibiting the thrombogenic or clotting ability of materials which are susceptible to interaction with an aromatic sulfonyl nitrene which comprises a. contacting the said material with a compound of the generic structure
 8. A process in accordance with claim 7 wherein the material is selected from the group consisting of polyethylene, polypropylene, latex, and polyethylene terephthalate, R is hydrogen and R1 is selected from the group consisting of hydrogen, chloride, bromide and alkyl of from one to three carbon atoms, inclusive, and R2 is a substance which inhibits thrombogenic activity.
 9. A process in accordance with claim 7 wherein the material is selected from the group consisting of polyethylene and polypropylene, R and R1 are hydrogen, and R2 is derived from 8-amino-1-naphthol-5,7-disulfonic acid.
 10. A process for inhibiting the thrombogenic or clotting ability of polyethylene which comprises a. contacting polyethylene with a compound of the generic structure 